Carbon nanotube powder HX-N2 - PRODUCTS - 青岛昊鑫新能源科技有限公司——石墨烯粉|碳纳米管导电剂|导电剂|石墨烯导电剂|石墨烯导电浆料|石墨烯导电剂|石墨烯多少钱一吨|石墨烯粉末|石墨烯电池|碳纳米管多少钱|碳纳米管的应用|碳纳米管|石墨烯|碳纳米管|碳纳米管导电浆料|天然石墨负极|人造石墨负极|

    Carbon nanotube powder HX-N2

    HX-N2

    产品简介:

    Product characteristics

    Carbon nanotubes can be seen as tubular one-dimensional nanomaterials that are curled by graphene and have excellent conductivity and mechanical properties. Carbon nanotubes have shown excellent performance in the electrical conductivity of lithium-ion batteries. Not only can the amount of conductive agents be significantly reduced, but the tubular conductive network formed can also effectively improve the performance of the electrode. Haoxin Technology has developed HX-N series of high-quality carbon nanotubes. The product has the characteristics of high purity, good dispersion, high stability, and excellent conductivity. It has obvious advantages in the application of lithium ion battery conductors. In the case of carbon nanotubes adding only Super-P10 %, It still shows superior conductivity to Super-P.


    Technical parameters


    project

    diameter

    purity

    length

    Specific surface area

    Indicator value

    8~15 nm

    >98%

    10~20 μm

    180~220 m2/g


    Use of recommendations

    This product can be added as a conductive agent to the positive or negative electrode of the battery. The recommended amount of addition is 0.5 % to 2 %.

    This product is a solid powder, easy to absorb moisture, please store and use in a dry environment, the use of dust inhalation should be strictly avoided. In order to achieve the best conductive effect, it is necessary to fully disperse in the solvent before use. It is recommended to use batch feed and ultrasonic or high-speed shear to fully disperse.